Pengaruh Alkalisasi Terhadap Kekuatan Impak Komposit Epoxy Berpenguat Serat Sisal

  • I Made Sukadana
  • I Putu Lokantara Lokantara
  • I Gede Putu Agus Suryawan
  • Ni Made Dwidiani

Abstrak

Abstractt
This study aims to determine the effect of alkali treatment on impact strength of sisal fiber reinforced epoxy
composites printed using the Hand Lay-Up method with random fiber orientation. The matrix used was 52-id
epoxy sikadur using a 30% fiber volume fraction. After testing, the impact strength increased by 32.06% in
treated sisal fiber reinforced epoxy composites compared to untreated sisal fiber composites. The impact
strength of the specimens treated with alkali was 0.0233 J/mm2, while the epoxy composite with untreated sisal
fiber had an impact strength of 0.0176/mm2. Based on these results, it can be concluded that the alkali treatment
had an effect on increasing the impact strength of the sisal fiber composites due to the formation of better bonds
due to a reduction in the lignin layer on the fibers so that the density of sisal fiber increased by 42.32% after
being treated and resulted in a better fiber structure. compact compared to fibers without alkali treatment..
Keywords: Composite, Natural Fiber, Sisal Fiber, NaOH, Hand Lay-Up, Impact Strength

##plugins.generic.usageStats.downloads##

##plugins.generic.usageStats.noStats##
Diterbitkan
2023-10-01
##submission.howToCite##
SUKADANA, I Made et al. Pengaruh Alkalisasi Terhadap Kekuatan Impak Komposit Epoxy Berpenguat Serat Sisal. Teknik Desain Mekanika, [S.l.], v. 12, n. 4, oct. 2023. ISSN 2302-5182. Tersedia pada: <https://ojs.unud.ac.id/index.php/mekanika/article/view/113366>. Tanggal Akses: 22 nov. 2024
##submission.howToCite.citationFormats##
Terbitan
Vol 12 No 4 (2023): Oktober 2023 : Teknik Desain Mekanika
Bagian
Articles

##plugins.generic.recommendByAuthor.heading##

1 2 > >>