Effect of Pressure on the Synthesis of Compound Ba0.7Ca0.3TiO3 on the Dielectric Constant
Abstract
Piezoelectric and ferroelectric ceramic materials are widely used for advanced technology. Barium Titanat is one of the ferroelectric materials that are still widely studied today. In this research, Ba0,7Ca0,3TiO3 was synthesized. The compound was synthesized by the solid reaction method with variations in pressure during the sample compacting process include 10, 20, and 30 kN. Samples in the form of solids (pellets) were calcined at 800 °C and sintered at 1000 °C for 4 hours respectively. The synthesized product was characterized by an LCR meter. The characterization results in the frequency range of 100-200000 Hz show that the pressure affects of the parameters value of the dielectric constant, especially at frequencies 100-10000 Hz. In that frequency range the dielectric constant decreases very sharply, then above 100 kHz the dielectric constant is almost unchanged with increasing frequency.
Downloads
References
[2] Edita Palaimiene, Jan Macutkevic, Juras Banys, Antoni Winiarski, Irena Gruszka, Janusz Koperski and Andrzej Molak, Crossover from Ferroelectric to Relaxor Behavior in Ba1−xCaxTiO3 (x = 0.17) System, Materials, vol. 13, 2854, 2020, pp. 1-11.
[3] Ch. Rayssi, S. El.Kossi, J. Dhahri, and K. Khirouni, Frequency and temperature-dependence of dielectric permittivity and electric modulus studies of the solid solution Ca0.85Er0.1Ti1-xCo4x/3O3 (0 x0.1), RSC Adv., vol. 8, 2018, pp. 17139-17150.
[4] F. K. Nisa, A. Jamaluddin, dan Y. Iriani, Pengaruh Doping Zirkonium (Zr) pada Konstanta Dielektrik dan Struktur Kristal BaZr x Ti1-x O3, Jurnal Fisika dan Aplikasinya, vol. 12, no. 1, 2016, pp. 24-26.
[5] A. Zaidah, Suwarni, A. Supriyanto, A. Jamaluddin, dan Y. Iriani, Pengaruh Temperatur Sintering pada Konstanta Dielektrik Barium Stronsium Titanat (Ba0,2Sr0,8TiO3) yang dibuat dengan Metode Reaksi Fasa Padat, Jurnal Fisika dan Aplikasinya, vol. 11, no. 2, 2015, pp. 82 -85.
[6] N. Nurhadi, A. Jamaluddin dan Y. Iriani, Pengaruh Variasi doping Lantanum pada Barium Titanat (Ba1-x Lax TiO3) Terhadap Struktur Mikro dan Sifat Ferroelektrik, Jurnal Teori dan Aplikasi Fisika, vol. 01, no. 02, Juli 2013.
[7] M. Istiqomah, A. Jamaluddin, dan Y. Iriani, Pembuatan Material Feroelektrik Barium Titanat (BaTiO3) Menggunakan Metode Solid State Reaction, Jurnal Fisika Indonesia, XVIII (53), 2014.
[8] Stuart O. Nelson and Andzej W, Kraszewski, Dielectric Properties of Material and Measurement Techniques, Drying Technology, vol. 8, no. 5, 1990, pp. 1123-1143.
[9] R. D. Safitri, Y. Subarwanti, A.Supriyanto, A. Jamaluddin, dan Y.Iriani, Pembuatan Material Ferroelektrik Barium Titanat (BaTiO3) menggunakan Metode Kopresipitasi, Jurnal Fisika dan Aplikasinya, vol. 12, no. 3, 2015, pp. 112-115.
[10] V. S. Vinila and Jayakumari Isac, Temperature and Frequency Dependence of Dielectric Properties of Superconducting Ceramic GdBa2Ca3Cu4O10.5, International Journal of Science and Research (IJSR), vol. 7, Issue 8, 2018, pp. 696-703.
[11] Sugiyono, Metode Penelitian Kuantitatif dan R&D, Alfabeta, Bandung, 2007.
[12] V. R. Mudinepalli, L. Feng, Wen-Chin Lin, and B. S. Murty, Effect of grain size on dielectric and ferroelectric properties of nanostructured Ba0.8Sr0.2TiO3 ceramics, Journal of Advanced Ceramics, vol. 4 (1), 2015, pp. 46-53.