The The Effect of UVC Irradiation on the Structure and Swelling Properties of Chitosan Membranes Exposed to Magnetic Fields
Abstract
Abstract – Research on the effect of UVC radiation exposure on the structure and swelling properties of chitosan membranes exposed to magnetic fields has been carried out. The membrane used is the 2% chitosan membrane that has been exposed to a magnetic field of 1.5 mT in a parallel direction for 2 hours at the time of its formation (formation reaction). Furthermore, the dry membrane obtained was cut to a certain size and irradiated by using UVC radiation for 5, 10, 15 and 30 minutes, each of which was given the names M1, M2, M3 and M4. A comparison is a 2% chitosan membrane with exposure to a magnetic field for 2 hours without exposure to UVC radiation, which is called the control membrane (M0). Characterizations conducted include thickness, swelling (water absorption) and FTIR spectrophotometer. FTIR analysis shows that the OH, NH, CH, C = O, CN, CO and COC functional groups observed on the M0 membrane as well as on the M1, M2, M3, and M4 membranes, with the peaks shifted to smaller or larger wavenumbers. The percentage of transmittance of these functional groups increases with increasing irradiation time from 5 to 15 minutes and decreases in 30 minutes irradiation.
Downloads
References
[2] D. D. Fernanda, Kitosan Sebagai Adsorben Perak (Ag) Pada Limbah Fixer Fotografi Rumah Sakit, Buletin Fisika, vol. 20, no.1, 2019, pp. 6-10.
[3] P. I. P. Putri, Efek Paparan Radiasi UV-C Terhadap Karakteristik Rapat Arus Difusi Ion Pada Membran Kitosan, Skripsi, Universitas Udayana, 2015.
[4] P. E. Winasri, Efek Lama Paparan Radiasi UV-C Terhadap Karakteristik I-V Membran Kitosan, Buletin Fisika, vol.15, no.1, 2015, pp. 24 – 30.
[5] P. I. P. Putri, Pengaruh Waktu Paparan Radiasi UV-C Terhadap Karakteristik Rapat Arus Difusi Ion Pada Membran Kitosan, Buletin Fisika, vol. 17, no.1, 2016, pp. 49 – 56.
[6] N. Kusumawati dan S. Tania, Pembuatan Dan Uji Kemampuan Membran Kitosan Sebagai Membran Ultrafiltrasi Untuk Pemisahan Zat Warna Rhodamin B, Molekul, vol. 7, no. 1, 2012, pp. 43 - 52.
[7] A. B. Kusumaningtyas, Pengaruh Temperatur Larutan Terhadap Krakteristik Rapat Arus-Beda Potensial Membran Kitosan, Buletin Fisika, vol. 17, no.2, 2016, pp. 16 – 24.
[8] R. Agustin, Pengontrolan Kecepatan Motor DC Pada Penyimpanan Tempe Menggunakan Sinar Ultraviolet Berbasis Kontrol Logika Fuzzy, Skripsi, Universitas Brawijaya, 2013.
[9] S. Pratiwi dan P. Husni, Artikel Tinjauan: Potensi Penggunaan Tanaman Indonesia Sebagai Bahan Aktif Tabir Surya, Farmaka, vol.15, no.4, 2017, pp. 18-25.
[10] I. A. P. I. Gayatri, Pengaruh Paparan Medan Magnet Dalam Pembuatan Membran Kitosan Terhadap Sifat Mekaniknya, Skripsi, Universitas Udayana, 2018.
[11] E. Puspawiningtiyas dan D. Neni, Kajian Sifat Fisik Film Tipis Nata De Soya Sebagai Membran Ultrafiltrasi, Techno, vol.12, no.1, 2011, pp. 01-07.
[12] Y.Wang, et. al, Chitosan Membranes Filled by GPTMS-Modified Zeolite Beta Particles with Low Methanol Permeability for DMFC, Chemical Engineering and Processing 49, 2010, pp. 278–285.