Efek perlakuan pack carburizing dan media korosif pada baja AISI 1045 terhadap laju korosi

  • I Ketut Suarsana Universitas Udayana
  • I Made Astika Universitas Udayana
  • I Gede Putu Agus Suryawan Universitas Udayana

Abstract

Corrosion is a destructive symptom that affects the properties of a metal, which means that the physical properties and quality of the metal decrease due to the electrochemical reaction between the metal and its environment so that the strength of the metal decreases. Corrosion control can be used to avoid the negative impact of corrosion, through the pack carburizing treatment method. The material used in this research is AISI 1045 steel. To determine the effect of pack carburizing on the corrosion rate of steel, the research was carried out by varying the suhue of the carburizing pack and corrosive media. In this study, the pack carburizing process with suhue variations used was 750°C, 850°C, 950°C and the corroding media used were air, fresh water and sea water. This was observed in accordance with the application of AISI 1045 material. The corrosive process through corrosive media was carried out for 720 hours. The results showed that pack carburized steel at a temperature of 950°C had a lower corrosion rate than pack carburized steel at 750°C. Also, air corrosive media provides a lower corrosion rate compared to seawater corrosion rate.

Downloads

Download data is not yet available.

References

[1] K. Trethewey and J. Chamberlain, Korosi. PT Gramedia Pustaka Utama, Jakarta, 1991.

[2] M. G. Fontana, Corrosion Engineering. Mc Graw Hill International Book Company, Singapura, 1967.

[3] K. Suarsana and I. N. Santhiarsa, Laju Korosi dengan Perubahan Besar Derajat Deformasi Plastis dan Media Pengkorosi Pada Material Baja Karbon, J. Ilm. Tek. Desain Mek., vol. 6, no. 3, pp. 290–304, 2017.

[4] D. Satria et al., Pengaruh Waktu Tahan Proses Pack Carburizing Baja AISI 3115 dengan Menggunakan Calcium Carbonat dan Batubara Sub Bituminous dan Mendapatkan Perlakuan Panas Quenching Media Pendingin Air, Rotasi, vol. 21, no. 2, p. 88, 2019, doi: 10.14710/rotasi.21.2.88-95.

[5] H. Hafni, Pengaruh Waktu Tahan Proses Pack Carburizing pada Baja Karbon Rendah dengan Menggunakan Calcium Carbonat dan Arang Tempurung Kelapa, Di Tinjau Dari Kekerasan, J. Tek. Mesin, vol. 5, no. 2, 2015.

[6] Supomo and Heri, Buku Ajar Korosi, Jurusan Teknik Perkapalan FTK. ITS Surabaya, 2003.

[7] W. Callister, Material Science and Engineering an Introduction 7 edition. JohnWiley and Sons. Inc., 2007.

[8] Yunaidi, Perbandingan Laju Korosi Pada Baja Karbon Rendah dan Stainless Steel Seri 201, 304, dan 430 Dalam Media Nira, Mek. dan Sist. Termal, vol. 1, no. 1, pp. 1–6, 2016.

[9] F. O. Aramide, S. A. Ibitoye, I. O. Oladele, and J. O. Borode, Pack Carburization of Mild Steel, Using Pulverized Bone As Carburizer: Optimizing Process Parameters, Leonardo Electron. J. Pract. Technol., vol. 9, no. 16, pp. 1–12, 2010.

[10] D. Kurniawan, Pengaruh Temperatur Pack Carburizing dan Media Pengkorosi Terhadap Laju Korosi Baja Aisi 1045, in Thesis Research, Udayana University, 2006.

[11] A. Yudha Kurniawan Afandi, Irfan Syarif Arief, Analisa Laju Korosi pada Pelat Baja Karbon dengan Variasi Ketebalan Coating,”J. Tek. Its, vol. 4, no. 1, pp. 1–5, 2015.
Published
2022-01-11
How to Cite
SUARSANA, I Ketut; ASTIKA, I Made; AGUS SURYAWAN, I Gede Putu. Efek perlakuan pack carburizing dan media korosif pada baja AISI 1045 terhadap laju korosi. Jurnal Energi Dan Manufaktur, [S.l.], v. 14, n. 2, p. 37-43, jan. 2022. ISSN 2541-5328. Available at: <https://ojs.unud.ac.id/index.php/jem/article/view/82224>. Date accessed: 26 june 2022. doi: https://doi.org/10.24843/JEM.2021.v14.i02.p01.
Section
Articles

Most read articles by the same author(s)