Karakterisasi Papan Partikel dari Kulit Buah Kakao (Theobroma cacao L.) dalam Variasi Jenis dan Konsentrasi Perekat
Article Sidebar
Main Article Content
Abstract
Particle board is an artificial board created by combining lignocellulosic chips/particles using pressed synthetic adhesive to obtain characteristics similar to solid wood. This research aims to determine the effect of the types and concentrations of adhesive that produces the best particle board characteristics. This research used a Randomized Block Design (RBD) with treatment variations between types of adhesive, namely PVAc, epoxy, and urea formaldehyde, as well as adhesive concentration levels consisting of 50%, 55%, 60%, and 65%, with a total of 12 levels. Each treatment was grouped into 2 based on the time the particle board was made to obtain 24 experimental units. The variables observed were physical properties which included: density, water content, water absorption capacity, and thickness expansion, then mechanical properties which included: modulus of elasticity, modulus of rupture, internal bonding, and screw holding strength. The data obtained was analyzed for diversity and continued with the Honestly Significant Difference Test (HSD). The research results showed that the type and concentration of adhesive had a very significant effect on water absorption capacity, thickness expansion, MOR, MOE, internal bonding, screw holding strength, had a significant effect on water content, and had no significant effect on density. Treatment of PVAc adhesive type with a concentration of 65% produces the best characteristics with a density value of 0.83 g/cm3, water content 12.81%, water absorption capacity 10.97%, thickness expansion 1.25%, MOR 33.38 kg/cm2, MOE 1490.83 kg/cm2, internal bonding 4.68 kg/cm2, and screw holding strength 4.85 kgf.
Keywords : Particleboard, types and concentrations of adhesive
Papan partikel merupakan papan buatan yang tercipta melalui penggabungan serpihan/ partikel lignoselulosa menggunakan perekat sintetis yang dipres sehingga memperoleh karakteristik yang mirip dengan kayu padat. Penelitian ini bertujuan untuk mengetahui pengaruh jenis dan konsentrasi perekat yang menghasilkan karakteristik papan partikel terbaik. Penelitian ini menggunakan Rancangan Acak Kelompok (RAK) dengan perlakuan variasi antara jenis perekat yaitu PVAc, epoksi, dan urea formaldehida, serta tingkat konsentrasi perekat yang terdiri dari 50%, 55%, 60%, dan 65%, dengan jumlah taraf sebanyak 12, masing-masing perlakuan dikelompokkan menjadi 2 berdasarkan waktu pembuatan papan partikel sehingga diperoleh 24 unit percobaan. Variabel yang diamati yaitu sifat fisis yang meliputi: kerapatan, kadar air, daya serap air, serta pengembangan tebal, kemudian sifat mekanik yang meliputi: Modulus of Elasticity, Modulus of Rupture, Internal Bonding, serta kuat pegang sekrup. Data yang diperoleh dianalisis keragamannya dan dilanjutkan dengan Uji Beda Nyata Jujur (BNJ). Hasil penelitian menunjukkan bahwa jenis dan konsentrasi perekat berpengaruh sangat nyata terhadap daya serap air, pengembangan tebal, MOR, MOE, internal bonding, kuat pegang sekrup, berpengaruh nyata terhadap kadar air, dan tidak berpengaruh nyata terhadap kerapatan. Perlakuan jenis perekat PVAc dengan konsentrasi 65% menghasilkan karakteristik terbaik dengan nilai kerapatan 0,83 g/cm3, kadar air 12,81%, daya serap air 10,97%, pengembangan tebal 1,25%, MOR 33,38 kg/cm2, MOE 1490,83 kg/cm2, internal bonding 4,68 kg/cm2, dan kuat pegang sekrup 4,85 kgf.
Kata kunci : Papan partikel, jenis dan konsentrasi perekat
Downloads
Article Details
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.
Seluruh artikel di Jurnal ini dapat disebarluaskan atas tetap mencantumkan sumber yang syah. Identitas judul artikel tidak boleh dihilangkan. Penerbit tidak bertangggung jawab terhadap naskah yang dipublikasikan. Isi artikel menjadi tanggung jawab Penulis.
References
Badan Pusat Statistik. 2021. Produksi kakao menurut kabupaten/kota di provinsi bali (ton) 2020-2022. Badan Pusat Statistik Provinsi Bali. https://www.bps.go.id.
Badan Pusat Statistik. 2022. Statistik Kakao Indonesia. Badan Pusat Statistik. https://bali.bps.go.id/indicator/54/352/1/produksi-kakao-menurut- kabupaten-kota-di-provinsi-bali.html.
Badan Standardisasi Nasional. 2006. SNI-03-2105-2006 Papan Partikel. Badan Standardisasi Nasional.
Dumanauw, J. F. 1984. Mengenal Kayu. PT. Gramedia.
Gultom, L. A., Dirhamsyah, dan Setyawati, D. 2013. Sifat fisik mekanik papan partikel jerami padi. Jurnal Hutan Lestari, 1(3), 458–465.
Indrayanti, L., Siska, G., dan Sijabat, F. 2023. Uji pendahuluan sifat fisika mekanika papan partikel kayu kawui (vernonia arborea) dengan tiga persentase perekat pvac (polyvinyl acetate). Agrienvi, 17(1), 27–36. https://doi.org/10.36873/aev.v17i1
Iskandar, M. I., dan Supriadi, A. 2013. Pengaruh kadar perekat terhadap sifat papan partikel ampas tebu. Jurnal Penelitian Hasil Hutan, 31(1), 19–26.
Lu, F., Rodriguez-Garcia, J., Van Damme, I., Westwood, N. J., Shaw, L., Robinson, J. S., Warren, G., Chatzifragkou, A., McQueen Mason, S., Gomez, L., Faas, L., Balcombe, K., Srinivasan, C., Picchioni, F., Hadley, P., and Charalampopoulos, D. 2018. Valorisation strategies for cocoa pod husk and its fractions. Current Opinion in Green and Sustainable Chemistry, 1–18. https://doi.org/10.1016/j.cogsc.2018.07.007
Malau, J. C., Sucipto, T., dan Iswanto, A. H. 2016. Kualitas papan partikel batang pisang barangan berdasarkan variasi kadar perekat phenol formaldehida. Peronema Forestry Science Journal, 5(1), 1–9.
Maloney, T. M. 1993. Modern Particle Board and Dry Process Fibre Board Manufacturing. Miller Freeman Inc.
Massijaya, M. Y., Hadi, Y. S., dan Marsiah, H. 2005. Pemanfaatan limbah kayu dan karton sebagai bahan baku papan komposit. In Laporan Penelitian Lembaga Penelitian dan Pemberdayaan Masyarakat.
Mawardi, I. 2009. Mutu papan partikel dari kayu kelapa sawit (kks) berbasis perekat polystyrene. Jurnal Teknik Mesin, 11(2), 91–96.
Mustofa, K., Kurdiansyah, K., dan Thamrin, G. A. R. 2020. Efek variasi perbandingan komposisi perekat resin limbah gergajian kayu jabon (anthocephalus cadamba) dan kayu sengon (paraserianthes falcataria) terhadap sifat fisika dan mekanika papan partikel. Jurnal Sylva Scienteae, 3(1), 127–139.
Nurdin, H., Hasanuddin, Waskito, dan Saddikin, M. 2019. Characteristics of particleboard from waste nypa fruticans wurmb. Journal of Physics: Conference Series, 1387(1), 1–7. https://doi.org/10.1088/1742-6596/1387/1/012103
Pradana, I. G. M. T., Harsojuwono, B. A., dan Hartiati, A. 2018. Karakteristik papan partikel kulit buah kakao (theobroma cacao l.) Pada variasi konsentrasi perekat polyvinyl acetate. Jurnal Rekayasa Dan Manajemen Agroindustri, 6(1), 82–91.
Purnamawati, H., dan Utami, B. 2014. Pemanfaatan limbah kulit buah kakao (theobroma cacao l.) Sebagai adsorben zat warna rhodamin b. Prosiding Seminar Nasional Fisika dan Pendidikan Fisika, 5(1), 12–18.
Purwanto, D. 2016. Sifat fisis dan mekanis papan partikel dari limbah campuran serutan rotan dan sebuk kayu. Jurnal Riset Industri, 10(3), 125–133.
Rangkuti, Z. 2011. Pembuatan dan karakteristik papan partikel dari campuran resin polyester dan serat kulit jagung. Universitas Sumatera Utara.
Sari, H. P., dan Mora, M. 2020. Analisis sifat fisis dan mekanis papan partikel dari serbuk kayu bayur (pterospermum javanicum) dan serbuk kulit kakao (theobroma cacao l) bertulang anyaman bambu. Jurnal Fisika Unand, 9(3), 368–374.
Sedayu, B. B., Widianto, T. N., Basmal, J., dan Utomo, B. S. B. 2008. Pemanfaatan limbah padat pengolahan rumput laut gracilaria sp. untuk pembuatan papan partikel. Jurnal Pascapanen dan Bioteknologi Kelautan dan Perikanan, 3(1), 1–10.
Septiani, E., Indrayani, Y., dan Setyawati, D. 2022. Sifat fisik dan mekanik papan partikel dari campuran serbuk gergaji dan ampas tebu (baggase) pada berbagai konsentrasi perekat urea formaldehida. Jurnal Lingkungan Hutan Tropis, 1(4), 1053–1063.
Setyo, H., Intang, N., dan Sudibyo, G. H. 2008. Variasi komposisi kerapatan partikel dan jumlah perekat terhadap karakteristik papan komposit limbah kayu aren–serbuk gergaji. Dinamika Rekayasa, 4(2), 99–114.
Siregar, S. H., Hartono, R., Sucipto, T., dan Iswanto, A. H. 2014. Variasi suhu dan waktu pengempaan terhadap kualitas papan partikel dari limbah batang kelapa sawit dengan perekat phenol formaldehida. Peronema Forestry Science Journal, 3(1), 10–17.
Siska, G., Sarinah, dan Bangun, D. L. 2018. Kualitas papan partikel dari limbah gergajian kayu bangkirai (shorea laevis ridl). Jurnal Hutan Tropika, 13(1), 25–30.
Sitanggang, J. P., Sucipto, T., dan Azhar, I. 2015. Pengaruh kadar perekat urea formaldehida terhadap kualitas papan partikel dari kayu gamal (gliricidia sepium). Peronema Forestry Science Journal, 4(2), 166–174.
Sobamiwa, O., and Longe, O. G. 1994. Utilization of cocoa-pod pericarp fractions in broiler chick diets. Animal Feed Science and Technology, 47, 237–244.
Sudiryanto, G. 2015. Pengaruh suhu dan waktu pengempaan terhadap sifat fisik dan mekanik papan partikel kayu sengon (paraserianthes falcataria (l.) nielsen). Jurnal Disprotek, 6(1), 67–74.
Sugiartha, I. W., Rofaida, A., Rawiana, S., Pathurahman, P., dan Suparjo, S. 2022. Pemanfaatan limbah plastik polyethylene terephthalate (pet) dan serbuk bambu sebagai bahan pengisi papan partikel. Spektrum Sipil, 9(2), 160–166. https://doi.org/10.29303/spektrum.v9i2.248
Sulastiningsih, I. M., Novitasari, N., dan Turoso, A. 2006. Pengaruh kadar perekat terhadap sifat papan partikel bambu. Jurnal Penelitian Hasil Hutan, 24(1), 1–8.